Marca: | PERFLEX |
Certificação: | CE/ROHS/ISO9001 |
Número do modelo: | PXF-500/SIKA 315 |
Quantidade de ordem mínima: | 200 baldes |
---|---|
Detalhes da embalagem: | 5 L/10L/20L pelo balde |
Tempo de entrega: | 7days ao redor |
Habilidade da fonte: | De 20000 toneladas anualmente |
Material: | Endurecedor da resina + do isocyanate de Polyaspartic | Relação da mistura: | : B: C= 100: 20: 50 |
---|---|---|---|
Cor: | transparente | Característica: | Bom ligamento | resistência do tempo |
Pacote: | 5L | 10L | 20L/balde | Aplicação: | Parque | Estrada | Jardim | Revestimento da piscina |
Realçar: | Revestimento transparente do assoalho de Polyaspartic,Revestimento do assoalho de Polyaspartic antienvelhecimento,Assoalho de Polyaspartic que reveste o pacote 20L |
5L 10L 20L Package Transparent Polyaspartic Floor Coating Anti-aging No-yellowing Mapei Replacement
INTRODUCTION: PXF-500 is a three-component reaction curing transparent floor coat made of polyaspartic resin, HDI hardener and organic micro bead materials, with special organic micro bead and multi-functional chemical, it can provide strong adhesion and substrate adhesion when overcoat on epoxy or polyurethane substrate, and super wear and scratch resistance of the coating layer. It’s has good anti- QUV properties, anti-aging and yellowing resistance and chemical resistance performance, the best choice for heavy duty vehicle flooring indoor or outdoor.
FEATURE
1- Low maintenance
2- Excellent UV resistance
3- Low VOC-content, low odor
4- Durable, impermeable and seamless
5- Smooth glossy finish, optional slip resistant semi-gloss finish
6- Unique UV blocker technology provides superior ultraviolet light screening
APPLICATION: Typically used in light to heavy-duty traffic areas
▪ Laboratories, Life Sciences, Pharmaceutical industries and Health Care industry.
▪ Education (e.g. Schools and Universities).
▪ Leisure & Culture (e.g. Museums, Stadiums).
▪ Retail (e.g. Shopping Malls).
▪ Manufacturing facilities and warehouses.
Part A | Resin | Part B | Hardener |
Appearance | Transparent | Appearance | Transparent |
Viscosity 25 ℃ | 1200mpas | Viscosity 25 ℃ | 12mpas |
Specific gravity 25 ℃ | 1.15 | Specific gravity 25 ℃ | |
Solid content | 99% | Solid content |
Part D: Organic Micro Bead Materials
PROPERTIES AFTER CURING
7-day hardness | Shore D 68 |
Abrasion (CS17 wheel 750g, 500r) / Mg | 25 |
Elongation at break (%) | 15 |
Tensile strength (MPA) | 23 |
Concrete adhesion (MPA) | 2.2 |
Acid resistance | no change in 5% sulfuric acid |
Alkali resistance | no change in 10% sodium hydroxide |
Impact resistance (1000g, 1m) | Pass |
- BLEND RATIO BY WEIGHT
A : B : D = 100 : 20 : 50
- WORKING TIME
Temperature (℃) | 25 | 30 | |
Mixed service life (min) | 20 | 15 |
- CONSTRUCTION CONDITIONS
Construction amount: strictly control the amount in 0.05 ~ 0.1kg/m2 to avoid accumulation, otherwise the foaming is serious
Construction conditions:
Ambient temperature: 0 ℃ - 35 ℃, ambient humidity: ≤ 85%
Substrate temperature: must be more than 3 ℃ above air dew point temperature
Cleaning agent: Asparagus polyurea standard diluent
Note: this material has very high requirements for construction, and can only be operated after professional training of our company before use.
- DRY TIME AND RECOAT INTERVAL
Temperature (℃) : 25
Walking opening hours (HRS): 8
Vehicle opening hours (HRS) : 2
Recoat interval hours (HRS): 2
The above data is only for guidance, and the real curing time is highly related to the ambient temperature and humidity.
- SURFACE TREATMENT
Clean water to remove salt and other water-soluble contaminants.
Use proper detergent and degreaser to remove grease.
Clean and dry the surface before construction.
Pay attention to the painting interval between the primer and the construction.
Storage time: 12 months
Storage temperature: 5 ℃ - 35 ℃
Part A: 3kg | Part B: 0.6kg | Part D: 1.4kg